Cold Drawn Seamless Carbon Steel Pipe A106 Grade B For High Temperature Boiler - China

Cold Drawn Seamless Carbon Steel Pipe A106 Grade B For High Temperature Boiler ASTM A106 grade B Seamless Pressure Pipe (ASME SA106) is used in power plants, boilers, petrochemical plants, oil and gas refineries, and ships where the piping must transport fluids and gases that exhibit high pressures and temperatures.

At XOOS, we distribute pipe that meets the latest chemistry standards from ASME.

1 - Standards: ASTM A106 Standard Specification for Seamless Carbon Steel Pipe for High-Temperature Service 2 - Application: Oil, Gas and water delivery; Refinery, Boiler and Mechanical equipment manufacture; Structure construction; drilling, ship building and etc.

3 - Ordering Information Quantity (feet, meters, or number of lengths), Name of material (seamless carbon steel pipe), Grade (Grade B), Manufacture (hot-finished or cold-drawn), Size (NPS/DN and weight class or schedule number, or both; outside diameter and nominal wall thickness; or inside diameter and nominal wall thickness), Special outside diameter tolerance pipe, Inside diameter tolerance pipe, over 10 in, (250mm) ID.

Length (specific or random), Optional requirements, Test report required, Special requirements.

4 - Chemical Requirements - - - - Chemical Requirements | Grade | Composition, % | C | Mn | P | S | Si | Cr | Cu | Mo | Ni | V | max | max | max | min | maxC | maxC | maxC | maxC | maxC | Grade B | 0.3B | 0.291.06 | 0.035 | 0.035 | 0.1 | 0.4 | 0.4 | 0.15 | 0.4 | 0.08 | - - - - A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.

B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.

C These five elements combined shall not exceed 1%.

5 - Mechanical Properties Tensile Strength, min: 60ksi/415MPa Yield Strength, min: 35ksi/240MPa 6 - Manufacturing Process Raw Material Inspection Cold Centering Heating Piercing & Rolling SIzing Heat Treatment Testing Finishing NDE Visual & Dimension Inspection Marking Storing & Shipping 7 - Available Size Range - - - - OD | Thickness | mm | inch | mm | SCH | 21.3~1422 | 1/2''~ 56'' | 2.11~140 | SCH10 | *If the steel grades and size you are looking for are not listed above, please contact us for further information.

| - - - - 8 - Heat Treatment Hot-finished pipe need not be heat treated.

Cold-drawn pipe shall be heat treated after the final cold draw pass at a temperature of 1200F(650C) or higher.

9 - Supplementary Requirements S1 Product Analysis S2 Transverse Tension Test S3 Flattening Test, Standard S4 Flattening Test, Enhanced S5 Metal Structure and Etching Test S6 Carbon Equivalent S7 Heat Treated Test Specimens S8 Internal Cleanliness-Government Orders S9 Requirements for Carbon Steel Pipe for Hydrofluoric Acid Alkylation Service

Company Contact:

• Posted By: Xi an Overseas Oilfield Services Co., Ltd.

• Phone: 86-29-89584808

• Address: C-1102, Van Metropolis, No. 35, Tangyan Road, Xi'an, China, Xi an, shanxi , China

• Email:

• Website: https://www.seamlessalloysteelpipe.com

• Business Description: Since 2008, XOOS has been engaged in seamless alloy steel pipe, carbon steel pipe, and stainless steel pipe distrubtion industry.
  
  With the support of our strategic partners like Chengde Group, Hengyang Group, TPCO, Baosteel, Jiuli, etc.