The Difference Between 6061 Aluminum Alloy T6 And T651 - China

The main alloying elements in 6061 aluminum alloy are magnesium and silicon, which have medium strength, good corrosion resistance, weldability, and good oxidation effect.

It is widely used in various industrial structural parts that require a certain strength and high antimicrobial corrosion.

Its main chemical components are: Cu0.15-0.4-, Si0.4-0.8, Fe0.7-, Mn0.15-, Mg0.8-1.2-, Zn0.25-, Cr0.04-0.35-, Ti0 - The difference between the state of 15-, 6061 aluminum plate T6 and T651 is that under normal circumstances, the internal stress of T6 will be relatively large, and the processing will be deformed.

The most suitable state for processing should be T651 - It is stretched on the basis of T6 to eliminate Internal stress.

　 The difference between the state T6 and T651 of 6061 aluminum plate is that under normal circumstances, the internal stress of T6 will be relatively large, and the processing will be deformed.

The most suitable state for processing should be T651 - It is stretched on the basis of T6 to eliminate internal stress 6061 The main alloying elements of aluminum alloy are magnesium and silicon, and form Mg2Si phase.

If it contains a certain amount of manganese and chromium, it can neutralize the bad effects of iron; sometimes a small amount of copper or zinc is added to improve the strength of the alloy, and Does not significantly reduce its corrosion resistance; there is a small amount of copper in the conductive material to offset the adverse effects of titanium and iron on the conductivity; zirconium or titanium can refine the grain and control the recrystallization structure; in order to improve the machinability Performance, lead and bismuth can be added.

Mg2Si is dissolved in aluminum to make the alloy have artificial age hardening function.

The main alloying elements in 6061 aluminum alloy are magnesium and silicon, which have medium strength, good corrosion resistance and weldability, The oxidation effect is better.

　 6061t6 is a commonly used aluminum alloy state.

Generally, unless otherwise specified, it is generally 6061t6 state, while 6061t651 is the best feature of 6 series aluminum alloys.

It is a fighter in 6000 series aluminum alloys.

It has excellent processing performance.

Excellent welding characteristics and electroplating, good corrosion resistance, high toughness and no deformation after processing, compact material without defects and easy polishing, easy color film, excellent oxidation effect and other excellent characteristics.

　 6061-T651 is the main alloy of 6061 aluminum alloy.

It is a high-quality aluminum alloy product produced by heat treatment and pre-stretching process.

Although its strength cannot be compared with the 2XXX series or 7XXX series, its magnesium and silicon alloys have many characteristics.

Representative uses of T651 include aerospace fixtures, electrical fixtures, and communications.

It is also widely used in automated mechanical parts, precision machining, mold manufacturing, electronics and precision instruments, SMT, PC board solder carriers, and so on.

Company Contact:

• Posted By: Mingtai Aluminum

• Phone: 18538303430

• Address: No/6 Changchun Road , Zhengzhou , Henan , China

• Email:

• Business Description: Henan Mingtai Aluminum Co., Ltd. is a large-scale aluminum foil manufacturer in China, a listed company, and is the leading large-scale private aluminum foil production and export in Henan.
  
  The 8006 aluminum foil produced by the company has the advantages of high cup convex value, high heat sealing strength, no pinhole, good sealing, etc.
  
  It is especially suitable for the production of wrinkle-free lunch boxes.
  
  The only manufacturer that can produce high-end aerospace dining box aluminum foil, in addition, the quality of the 1 series, 3 series, 5 series, 8 series aluminum foil produced is also far ahead, and at the same time, it is the aluminum foil raw material for various aluminum lunch box manufacturers at home and abroad.
  
  Supplier.